Veneer hot press is widely used in wood processing, decoration, building materials and many other fields. In use, it is necessary to pay attention to timely maintenance to avoid problems in the use of hot press, especially in cleaning.

After using the hot press, please make sure to check to ensure that there will be no problems in the next use, and it is necessary to clean the hot press frequently. If the professional hot press manufacturer does not clean the hot press in time, the appearance of the hot press will be damaged. There is a lot of dust, which will cause a lot of damage to the hot press. In short, be sure to check the hot press after use, because the cause of the hot press problem is that there is no daily check, so it will lead to hot press problems. Clean and maintain the hot press properly to improve work efficiency. This is where users and friends should pay attention when using hot press.

Positive pressure on the basis of negative pressure, with supporting glue, on the processing of PVC series, its linear place and Posting force is not comparable to negative pressure equipment, because of its large pressure. Low temperature, short film pressure time, processing of negative pressure set

The deformation problem of the workpiece (large area workpiece) during the preparation of the workpiece has greatly reduced the deformation degree of the workpiece. Using modern electronic new product control, after adjustment, the processing processes of entering, lifting, heating, vacuum, film pressure, film stripping, and falling can be completed actively. It is mainly driven by oil pressure and compressed air, so it is necessary to meet the air pressure and gas volume, and the frame is composed of all steel plates, all the structure is reasonable, and the two worktables can be used back and forth, or can be used alone. Vacuum adjustable

Protection method of veneer hot press

1, take off the hot press plate, brush the rust with a steel brush, and then use diluted hydrochloric acid (concentration 15% ~ 20%) to eradicate the rust, Wuxi double-sided hot press to make the pressure plate reveal metal color.

2, surfacing welding with 5mm 422 electrode in corrosion area. Because one side of the surfacing will form a zigzag plate, it is recommended to use two sides of the surfacing, so that the stress of the welding pile counteracts each other.

3. Planing both sides of the surfacing pressure plate on the double planer, the planing amount is 0. 5 mm.

4. If the plug welding cracks due to gouging, it is necessary to excavate. It is also said that after the double-sided plane, each pressure plate should be checked for steam test pressure one by one, found + existing water, and marked. After the experimental steam quenching, the Angle grinder is used to form a long groove or round groove at the water balloon weld for surfacing welding.